1, The specification of the product including basic size information, electrical and mechanical properties.
| Basic size information |
| Color |
White |
| Pitch |
1.25mm |
| Mating lock |
without |
| Material |
PA66 |
| Flammability |
UL94V-0 |
| Wire Insulation Diameter |
1.00mm Max. |
| Mounting side |
Standard on-Board |
| Terminals material |
phosphor bronze, tin-plated/gold-flash finish |
| |
| Electrical properties |
| Current Rating |
1A AC, DC |
| Voltage Rating |
150V AC, DC |
| Contact Resistance |
30mΩ Max |
| Insulation Resistance |
500mΩ min |
| Withstanding Voltage |
500V AC/minute |
| |
| Mechanical properties |
| Operating Temperatureemperature range |
-25℃ to 85 ℃ |
| Other information please kindly check the following picture. |
2, Drawings & testing report
|
3. Ratings & Applicable Wires
| Item |
Standard |
| Rated Voltage (Max.) |
125V AC/DC |
Insulation O.D. 0.90mm (Max.) |
| Rated Current (Max.) And Applicable Wires |
AWG#28 |
1A AC/DC |
| AWG#30 |
1A AC/DC |
| AWG#32 |
1A AC/DC |
| Ambient Temperature Range |
-25℃ ~ +85℃* |
*: Including terminal temperature rise
4. Electrical Performance
| Test Description |
Procedure |
Requirement |
| 4-1 |
Contact Resistance
|
Mate connectors, measure by dry circuit, 20mV (max), 10mA.(Based upon JIS C5402 5.4) |
20mΩ (Max.) |
| 4-2 |
Insulation Resistance |
Mate connectors, apply 500V DC between adjacent terminal or ground. (Based upon JIS C5402 5.2/MIL-STD-202 Method 302 Cond. B) |
100MΩ (Min.) |
| 4-3 |
Dielectric Withstanding Voltage |
Mate connectors, apply 500V AC (rms) for 1 minute between adjacent terminal or ground. (Based upon JIS C5402 5.1/MIL-STD-202 Method 301) |
No Breakdown. |
| 4-4 |
Contact Resistance on Crimped Portion |
Crimp the applicable wire on to the terminal, measure by dry circuit, 20mV (Max.)., 10mA. |
5mΩ (Max.) |
5. Mechanical Performance
| Test Description |
Procedure |
Requirement |
| 5-1 |
Actuator Insertion & Withdrawal Force |
Insert and withdraw connectors at the speed rate of 25±3mm / minute. |
Refer to paragraph 7 |
| 5-2 |
Crimping Pull Out Force |
Fix the crimped terminal, apply axial pull out force on the wire at the speed rat of 25±3mm / minute.(Based upon JIS C5402 6.8) |
AWG#28 |
1.0kgf (Min) |
| AWG#30 |
0.8kgf (Min) |
| AWG#32 |
0.5kgf (Min) |
| 5-3 |
Terminal Insertion Force. |
Insert the crimped terminal into the housing. |
0.50kgf (Max.) |
| 5-4 |
Terminal/Housing Retention Force. |
Apply axial pull out force at the speed rate of 25±3mm / minute on the terminal assembled in the housing. |
0.50kgf (Min.) |
| 5-5 |
Pin Retention Force |
Apply axial push force at the speed rate of 25±3mm / minute |
0.50kgf (Min.) |
| 5-6 |
Durability |
When mated up to 50 cycles repeatedly by the rate of 10 cycle per minute. |
Contact Resistance 40mΩ (Max.) |
| 5-7 |
Vibration |
Amplitude: 1.5mm P-P
Sweep time: 10-55-10 Hz in 1 minute Duration: 2 hours in each X.Y.Z. axes.
(Based upon MIL-STD-202 Method 201A)
|
Appearance No Damage.
Contact Resistance 40mΩ (Max.)
Discontinuity 1 μsec.(Max.)
|
| 5-8 |
Physical Shock |
490m/s²｛50G｝,3 strokes in each X.Y.Z. axes. (Based upon JIS C0041/MIL-STD-202 Method 213B Cond. A) |
|
|
6. Environmental Performance And Others
| Test Description |
Procedure |
Requirement |
| 6-1 |
Temperature Rise |
Carrying rated current load.(Based upon UL 498) |
30℃(Max.) |
| 6-2 |
Heat Resistance |
85±2℃,96 hours (Based upon JIS C0021/MIL-STD-202 Method 108A Cond. A) |
Appearance No Damage.
Contact Resistance 40mΩ (Max.)
|
| 6-3 |
Cold Resistance |
-25±3℃,96 hours (Based upon JIS C0020) |
| 6-4 |
Humidity |
Temperature: 40±2℃
Relative Humidity : 90~95%
Duration: 96 hours
(Based upon JIS C0022/MIL-STD-202 Method 103B Cond. B)
|
Appearance No Damage.
Contact Resistance 40mΩ (Max.)
Insulation Resistance 10MΩ (Min.)
Dielectric Withstanding Voltage Must meet 4-3
|
| 6-5 |
Temperature Cycling |
5 cycles of:
a) -55℃ 30 minutes
b) +85℃ 30 minutes
(Based upon JIS C0025)
|
Appearance No Damage.
Contact Resistance 40mΩ (Max.)
|
| 6-6 |
Salt Spray |
Tin-plated 12 hours / Gold- plated 24 hours exposure to a salt spray from the 5±1% solution at 35±2℃. (Based upon JIS C0023/MIL-STD-202 Method 101C Cond. B) |
| 6-7 |
SO2 Gas |
24 hours exposure to 50±5ppm.
SO2 gas at 40±2℃.
|
| 6-8 |
NH3 Gas |
40 minutes exposure to NH3 gas evaporating from 28% Ammonia solution. |
| 6-9 |
Solderability |
Soldering Time: 5±0.5 sec.
Solder Temperature: 245±5℃
|
Solder Wetting 95% of immersed area must show no voids, pin holes |
| 6-10 |
Resistance to Soldering Heat |
When reflowing
Refer to paragraph 8
Solder iron method
Soldering Time: 5±0.5 sec.
Solder Temperature: 370℃ ~ 400℃
|
Appearance No Damage. |
7. Actuator Insertion/Withdrawal Force
[Unit : kgf]
| Circuits |
At Initial |
Circuits |
At Initial |
| Insertion (Max.) |
Withdrawal (Min.) |
Insertion (Max.) |
Withdrawal (Min.) |
| Single |
0.22 |
0.02 |
10 |
2.20 |
0.20 |
| 02 |
0.44 |
0.04 |
11 |
2.42 |
0.22 |
| 03 |
0.66 |
0.06 |
12 |
2.64 |
0.24 |
| 04 |
0.88 |
0.08 |
13 |
2.86 |
0.26 |
| 05 |
1.10 |
0.10 |
14 |
3.08 |
0.28 |
| 06 |
1.32 |
0.12 |
15 |
3.30 |
0.30 |
| 07 |
1.54 |
0.14 |
20 |
4.40 |
0.40 |
| 08 |
1.76 |
0.16 |
30 |
6.60 |
0.60 |
| 09 |
1.98 |
0.18 |
|
|
|
|
3, FAQ
Q:Do you allow multiple design per setup?
A:Yes.We accept OEM service and allow multiple design per setup.
Q:How long does shipping take?
A:It depends on the destination location and quantity. In most developed world, delivery by Fed x/UPS/DHL is normally 3-5 days(excluding weekends).
Q: How is the goods packaged ?
A: Usually in bags, tube, pipe, plated & carton